Ingeo™ 3D850
| Category: | PLA , Polylactic Acid |
| Manufacturer: | NatureWorks® LLC |
| Trademark: | Ingeo™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 98aZlr_Ingeo3D850.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ingeo™ 3D850 is a grade developed for manufacturing 3D printer monofilament. This grade exhibits faster crystallization rates and is able to develop improved heat-resistance in 3D printed parts. This low color resin grade demonstrates the best performance in formulated systems designed to enhance toughness or heat-resistance. Monofilaments made with Ingeo 3D850 have excellent 3D printing characteristics such as precise detail, good adhesion to build plates, less warping or curling, and low odor. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 7.0 - 9.0 | g/10 min | ASTM D1238 |
| Relative Viscosity 1(30°C) | 4.00 | ASTM D5225 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2 | 2320 | MPa | ASTM D638 |
| Tensile Strength 3 | 50.3 | MPa | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength - MD 4(Yield) | 51.3 | MPa | ASTM D882 |
| Tensile Elongation - MD 5(Break) | 3.3 | % | ASTM D882 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 6 | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 7(0.45 MPa, Unannealed) | 80.0 - 90.0 | °C | ASTM E2092 |
| Glass Transition Temperature | 55.0 - 60.0 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 165 - 180 | °C | ASTM D3418 |
| Additional Information |
|---|
| 3D Printing Temperature: 190 to 230°CAnnealing Temperature: 80 to 130°CPrint Bed Temperature: None needed (or 50 to 70°C if applicable) |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 179 | °C | |
| Cylinder Zone 2 Temp. | 191 | °C | |
| Cylinder Zone 3 Temp. | 199 | °C | |
| Adapter Temperature | 199 | °C | |
| Melt Temperature | 210 | °C | |
| Die Temperature | 199 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 20 to 150 rpm |
| Note Message | |
|---|---|
| 1 . | 1.0 g/dL in chloroform |
| 2 . | 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 3 . | 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 4 . | 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 5 . | 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 6 . | 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| 7 . | 3D printed part, 100% in-fill, annealed at 110°C/15 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® B3WG6 GPX | BASF Corporation | Nylon 6 | Ultramid® |
| CP PRYME® Nylon 66 NN300HSL | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| LNP™ LUBRICOMP™ EL002 compound | SABIC Innovative Plastics | PEI | LNP™ LUBRICOMP™ |
| LubX® CV | Röchling Engineering Plastics SE & Co. KG | UHMWPE | LubX® |
| Sylvin 8299-80 Brown 7488 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |