INSPIRE™ 227
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Braskem Europe GmbH |
| Trademark: | INSPIRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 97cRVp_INSPIRE-227.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INSPIRE™227 high-performance polymer combines good processing performance, excellent stiffness and low crystal point content, and is used for extrusion processing of high-quality films. Main features:
please consult the regulations for complete details. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.2 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Puncture Energy (50 µm) | 0.500 | J | ASTM D5748 |
| Film Puncture Force (50 µm) | 42.0 | N | ASTM D5748 |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 50 µm | 1170 | MPa | ASTM D882 |
| 2% secant, TD : 50 µm | 1140 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 50 µm | 27.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm | 41.0 | MPa | ASTM D882 |
| MD : Break, 50 µm | 38.0 | MPa | ASTM D882 |
| TD : Break, 50 µm | 39.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 250 | % | ASTM D882 |
| TD : Break, 50 µm | 6.0 | % | ASTM D882 |
| Dart Drop Impact (50 µm) | 50 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm | 14 | g | ASTM D1922 |
| TD : 50 µm | 24 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 162 - 166 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm) | 32 | ASTM D2457 | |
| Haze (50.0 µm) | 23 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 230 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 模具间隙：1.0 mm 熔体温度：230°C 放大比：2.5 比 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP562 | Supreme Petrochem Ltd. | PS (IRPS) | SUPREME Specialty PS |
| Moplen HP521J | LyondellBasell Industries | PP Homopolymer | Moplen |
| NEFTEKHIM PP 4344N | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Next Nylon 6 Industrial Series NGF30-02BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Industrial Series |
| Hytrel® G4078 NC010 | DuPont Performance Polymers | TPC-ET | Hytrel® |