FORMULA P 6007
| Category: | PP, High Crystal , High Crystallinity Polypropylene |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | FORMULA P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 97T8Fb_FORMULA-P-6007.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FORMULA P 6007 is a highly crystalline polypropylene product,. It is available in Europe. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.5 - 1.8 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 25.0 | MPa | ISO 527-2 |
| Fracture | 21.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 45 | % | ISO 527-2 |
| Flexural Modulus | 1700 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 50.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 8.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 72.0 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 25 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 - 245 | °C | |
| Mold Temperature | 20.0 - 40.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 6594B-G80E-M | TSRC Corporation | SEBS | T-Blend® |
| VYLOPET® EMC132-01 | TOYOBO America, Inc. | PC+PBT | VYLOPET® |
| Ebalta ebatemp / PUR 5 | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| INEOS Wire & Cable BPD8063 | INEOS Olefins & Polymers Europe | LDPE | INEOS Wire & Cable |
| Cellasto® MH24-65 | BASF Polyurethanes GmbH | TPU, Unspecified | Cellasto® |