Order Products : sales@su-jiao.com
KOPA® KN333MT30BL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Kolon Plastics, Inc. |
| Trademark: | KOPA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 97S5vG_KOPA-KN333MT30BL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KOPA® KN333MT30BL is a Polyamide 66 (Nylon 66) product filled with 30% mineral. It is available in Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.80 | % | ASTM D955 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 125 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 74.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 8.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 4120 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 118 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 240 | °C | |
| 1.8 MPa, Unannealed | 230 | °C | |
| Peak Melting Temperature | 255 | °C | ASTM D1525 |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.40 | ASTM D150 | |
| Arc Resistance | 133 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Capilene® M 50 F | Carmel Olefins Ltd. | PP Homopolymer | Capilene® |
| EPO-TEK® H62 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Hostacom BG722AC (z) | LyondellBasell Industries | PP Copolymer | Hostacom |
| Infino NH-1024 | LOTTE ADVANCED MATERIALS CO., LTD. | PC+ABS | Infino |
| ULTEM™ 1010R resin | SABIC Innovative Plastics | PEI | ULTEM™ |