SABIC® LDPE 2602TH33
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 94oTd3_SABIC-LDPE-2602TH33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 2602TH33 is a grade with high optical properties and an increased density. The grade contains a very high level of anti block and a medium level of slip agent (E=erucamide). Films produced out of 2602TH33 combine low CoF with excellent optical properties. SABIC® LDPE 2602TH33 is particularly suitable for bread bags and other films for high speed automatic packaging lines. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.926 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.20 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| MD : 25 µm, blown film | 230 | MPa | ISO 527-3 |
| TD : 25 µm, blown film | 240 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, blown film | 12.0 | MPa | ISO 527-3 |
| TD : Yield, 25 µm, blown film | 12.0 | MPa | ISO 527-3 |
| MD : 25 µm, blown film | 25.0 | MPa | ISO 527-3 |
| TD : 25 µm, blown film | 20.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 25 µm, blown film | > 200 | % | ISO 527-3 |
| TD : Broken, 25 µm, blown film | > 500 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength (25.0 µm) 1 | 200 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking (25.0 µm) 2 | g | Internal method | |
| Re-blocking (25.0 µm) 3 | g | ISO 6383-2 | |
| Tear Strength 4 | ISO 6383-2 | ||
| MD : 25.0 µm | 90.0 | kN/m | ISO 6383-2 |
| TD : 25.0 µm | 40.0 | kN/m | ISO 6383-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 8.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film properties have been measured at film of 25 µm with a BUR of 3.The film has been produced on Kiefel IBC blown film line with 200 kg/h. Die size 200 mm, die gap 0.8 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| 2 . | Blown Film |
| 3 . | Blown Film |
| 4 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Multi-Flex® TPO 1047 MR | Multibase, A Dow Corning Company | TPO (POE) | Multi-Flex® TPO |
| Exact™ 4150 | ExxonMobil Chemical | Plastomer | Exact™ |
| K-Flex 3070 | Technovinyl Polymers India Ltd. | TPE | K-Flex |
| LNP™ LUBRICOMP™ DP003 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Axiall PVC 7533 | Axiall Corporation | PVC, Rigid | Axiall PVC |