Alathon® ETP H5057
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® ETP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 94Svm7_Alathon-ETP-H5057.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALATHON H5057 is a multi-purpose high-flow resin that exhibits enhanced low temperature impact performance, enhanced processing and thermal stability for fast cycling in multi-cavity stack molds, good color and organoleptic properties. Typical applications are rigid food containers such as cultured dairy product containers, margarine tubs, butter tubs, small frozen food containers and promotional drink cups. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.948 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.59 to 0.63 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 57 | g/10 min | ASTM D1238 |
| Spiral Flow | 53.8 | cm | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 69 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- | 795 | MPa | |
| 1% Secant | 683 | MPa | |
| Tensile Strength 2(Break) | 19.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 4.1 | % | ASTM D638 |
| Flexural Modulus 4 | ASTM D790 | ||
| -- | 1050 | MPa | |
| 1% Secant | 972 | MPa | |
| 2% Secant | 820 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 21 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | 330 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 64.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 118 | °C | ASTM D1525 |
| Peak Melting Temperature | 126 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 113 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STABAMID® 24 FE 2 | Solvay Polyamide & Intermediates | Nylon 66 | STABAMID® |
| Vexel B12GF15 | Custom Resins Group | PBT | Vexel |
| NORYL™ SE1GFN3 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| ACCUTECH™ CP0436T40L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| PAXOTHENE® NA205-15 | USI Corporation | LDPE | PAXOTHENE® |