Estane® MVT 75AT3 TPU
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 93G4bG_Estane-MVT-75AT3-TPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Type: Estane® MVT 75AT3 is a 75A aromatic Polyether-Based Thermoplastic Polyurethane (TPU) Features:
Process:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 5 sec) | 72 - 78 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 20.0 | mg | ASTM D3389 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Vapor Transmission | 400 | g/m²/24 hr | ASTM E96 |
| Water Vapor Transmission - Mocon 1(38°C) | 3000 | g/m²/24 hr | ASTM D6701 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Kofler Melting Temperature | 160 | °C | Internal method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Set (200% Strain) | 8 | % | ASTM D412 |
| Tensile Stress | ASTM D412 | ||
| 100% strain, 0.762mm | 4.10 | MPa | ASTM D412 |
| 300% strain, 0.762mm | 6.20 | MPa | ASTM D412 |
| Tensile Strength (Break, 0.762 mm) | 34.5 | MPa | ASTM D412 |
| Tensile Elongation (Break, 0.762 mm) | 700 | % | ASTM D412 |
| Tear Strength | |||
| 0.762 mm 2 | 62.8 | kN/m | ASTM D624 |
| Cracking | 20 | kN/m | ASTM D470 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Volume (23°C, 24 hr, in water) | 1.0 | % | ASTM D471 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -68.0 | °C | DSC |
| Melting Temperature | 136 | °C | DSC |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 177 | °C | |
| Cylinder Zone 2 Temp. | 182 | °C | |
| Cylinder Zone 3 Temp. | 188 | °C | |
| Cylinder Zone 4 Temp. | 193 | °C | |
| Adapter Temperature | 199 | °C | |
| Melt Temperature | 196 | °C | |
| Die Temperature | 199 | °C |
| Extrusion instructions |
|---|
| Dew Point: -40°CScreen Pack Recommendation: 20/40/80 |
| Note Message | |
|---|---|
| 1 . | 90% RH |
| 2 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC14-2233L | Spartech Polycom | Nylon 6 | Spartech |
| VESTAKEEP® 4000 FC30 | Evonik Industries AG | PEEK | VESTAKEEP® |
| Niblend S45 HG | Soredi S.p.a. | PC+ABS | Niblend |
| Karina WHITE PVC COMPOUND 846-10/114-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ KP004A compound | SABIC Innovative Plastics | Acetal (POM) Homopolymer | LNP™ LUBRICOMP™ |