| Glass Fiber Reinforced PA66 Compound with Heat Stabilized. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.30 - 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 180 | MPa | ISO 527-2 |
| Flexural Modulus | 8500 | MPa | ISO 178 |
| Flexural Stress | 260 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 245 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 260 - 280 | °C | |
| Front Temperature | 260 - 280 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makropol® PC A3 G20 PRTA010 PC315 | Petropol Industry and Trade of Polymers LTDA | PC | Makropol® PC |
| ALTECH® PA6 A 1000/510 IM | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Cariflex® IR0310 K | Kraton Polymers LLC | IR | Cariflex® |
| Formolene® 6535N | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| KER® 1502 | Synthos S.A. | SBR, Emulsion | KER® |