Osterlene® HD0954

Category:	HDPE , High Density Polyethylene
Manufacturer:	Osterman & Company
Trademark:	Osterlene®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	92LuVk_OsterleneHD0954.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

HD0954 is a general purpose HDPE injection molding resin with superior stiffness which allows for improved stack strength and is good for part thinwalling.

HD0954 has low viscosity for exceptional processability, shorter cycle times and energy savings.

This resin has low warpage for improved part quality and reliability. It has exceptional physical properties which provides impact resistance for demanding applications.

Addititives: Antioxidant

Osterlene HD0954 meets the requirements of the Food and Drug Administration, 21 CFR Section 177.1520. This regulation allows the use of this olefin polymer in "...articles or components of articles intended for use in contact with food." Specific limitations may apply. Contact your Osterman sales representative for more information.

General Information
Additive	Antioxidation
Features	Low warpage Rigidity, high Antioxidation Good strength
Agency Ratings	FDA 21 CFR 177.1520
Processing Method	Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity ¹	0.954	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) ²(190°C/2.16 kg)	9.0	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance (100% Igepal, Compression Molded)	< 10.0	hr	ASTM D1693B

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, Compression Molded)	66		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ³			ASTM D638
Yield, molding	28.5	MPa	ASTM D638
Yield, injection molding	22.3	MPa	ASTM D638
Fracture, molding	22.0	MPa	ASTM D638
Fracture, injection molding	16.0	MPa	ASTM D638
Tensile Elongation ⁴			ASTM D638
Yield, molding	8.0	%	ASTM D638
Yield, injection molding	9.0	%	ASTM D638
Fracture, molding	1200	%	ASTM D638
Fracture, injection molding	650	%	ASTM D638
Flexural Modulus - 1% Secant			ASTM D790
Molding	1230	MPa	ASTM D790
Injection Molding	960	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature ⁵	128	°C	ASTM D1525

Note Message
1 .	Compression Molded
2 .	Compression Molded
3 .	50 mm/min
4 .	50 mm/min
5 .	Compression Molded

Resin Grade	Manufacturer	Category	Trademark
Qenos PE GF7660	Qenos Pty Ltd	HDPE, MMW	Qenos PE
SILPURAN® 2450 A/B	Wacker Chemie AG	Silicone	SILPURAN®
EVICOM™ RG7/295H	INEOS Compounds	PVC, Flexible	EVICOM™
Geon™ Bold L5801	PolyOne Corporation	PVC Alloy	Geon™ Bold
LUVOCOM® 1850-8710	Lehmann & Voss & Co.	PBT	LUVOCOM®