XANTAR® LDS 3735
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | XANTAR® LDS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 92Iwnr_XANTARLDS3735.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Laser Direst Structuring (LDS), Impact Modified |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 13 | g/10 min | ISO 1133 |
| shrinkage- Flow | 0.60 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.35 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2100 | MPa | ISO 178 |
| Flexural Stress | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 35 | kJ/m² | ISO 179/1eA |
| 23°C | 45 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/4A | ||
| -20°C | 40 | kJ/m² | ISO 180/4A |
| 23°C | 50 | kJ/m² | ISO 180/4A |
| Multi-Axial Instrumented Impact Energy (23°C) | 40.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 121 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 141 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Relative Permittivity (1.00 GHz) | 2.88 | IEC 60250 | |
| Dissipation Factor (1.00 GHz) | 6.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (0.75 mm) | HB | IEC 60695-11-10, -20 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® PL-1131 | Sumitomo Bakelite Co., Ltd. | Phenolic | SUMILITE® |
| Sylvin 2953-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9714-70 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TOTAL Polystyrene 4440 (AS) | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |
| NHU-PPS 21310C/F | Zhejiang NHU Comp. Ltd. | PPS | NHU-PPS |