DIC.PPS FZ-2130
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | DIC Corporation |
| Trademark: | DIC.PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 927G17_DIC-PPS-FZ-2130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.56 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.27 | % | |
| Across Flow | 1.2 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 100 | ||
| R-Scale | 121 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ASTM D638 |
| Tensile Strength | 165 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 10000 | MPa | ASTM D790 |
| Flexural Strength | 250 | MPa | ASTM D790 |
| Compressive Strength | 190 | MPa | ASTM D695 |
| Poisson's Ratio | 0.36 | ||
| Coefficient of Friction 1 | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.35 | ||
| vs. Steel - Static | 0.35 | ||
| Flexural Elongation at Break | 2.7 | % | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 90 | J/m | ASTM D256 |
| Unnotched Izod Impact | 550 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 90°C | 2.3E-5 | cm/cm/°C | |
| Transverse : -30 to 90°C | 2.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 4.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 2.0E-3 | ASTM D150 | |
| Arc Resistance | 125 | sec | ASTM D495 |
| Comparative Tracking Index | 170 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 300 to 340 | °C | |
| Middle Temperature | 300 to 340 | °C | |
| Front Temperature | 300 to 340 | °C | |
| Mold Temperature | 120 to 150 | °C |
| Note Message | |
|---|---|
| 1 . | P=150KPa, V=0.3m/s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viton® F-605C | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| Nanguang TPU Y-80AX | Fujian Nanguang Light Industry Co., Ltd. | TPU, Unspecified | Nanguang TPU |
| Celanex® 3300D | Celanese Corporation | PBT | Celanex® |
| KANEKA H627 | Kaneka North America LLC | CPVC | KANEKA |
| LUVOCOM® 1-8070 VP | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |