Chemlon® 100 is a Polyamide 66 (Nylon 66) material. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Chemlon® 100: Flame Rated. Typical application of Chemlon® 100: Automotive |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (275°C/0.325 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 to 2.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.2 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 86.2 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 | % | |
| Break | 50 | % | |
| Flexural Modulus | 2860 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 220 | °C | |
| 1.8 MPa, Unannealed | 90.6 | °C | |
| Melting Temperature | 257 | °C | DSC |
| CLTE - Flow | 7.1E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec | UL 746 | ||
| 0.810 mm | 115 | °C | |
| 1.50 mm | 115 | °C | |
| 3.00 mm | 115 | °C | |
| RTI Imp | UL 746 | ||
| 0.810 mm | 75.0 | °C | |
| 1.50 mm | 75.0 | °C | |
| 3.00 mm | 85.0 | °C | |
| RTI Str | UL 746 | ||
| 0.810 mm | 95.0 | °C | |
| 1.50 mm | 95.0 | °C | |
| 3.00 mm | 95.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+18 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 18 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.810 mm) | V-2 | UL 94 | |
| Oxygen Index | 27 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 241 to 254 | °C | |
| Middle Temperature | 257 to 274 | °C | |
| Front Temperature | 263 to 282 | °C | |
| Nozzle Temperature | 263 to 279 | °C | |
| Processing (Melt) Temp | 263 to 279 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5210 | Spartech Polycom | PP Homopolymer | Spartech |
| Taitacell EPS 301Ss | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Borealis PP RC101 | Borealis AG | PP, Unspecified | Borealis PP |
| KEBATRON® PPS L1065X3 | BARLOG plastics GmbH | PPS | KEBATRON® |
| LNP™ STAT-KON™ DX03571 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |