Makropol® PC A3 HF UV BRCA008 PC307
| Category: | PC , Polycarbonate |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Makropol® PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 91SAWC_Makropol-PC-A3-HF-UV-BRCA008-PC307.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Makropol® PC A3 HF UV BRCA008 PC307 is a Polycarbonate (PC) material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Makropol® PC A3 HF UV BRCA008 PC307 are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 to 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 65.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus | 2300 | MPa | ASTM D790 |
| Flexural Strength | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 750 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 125 | °C | ASTM D648 |
| Vicat Softening Temperature | 145 | °C | ASTM D1525 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-1 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LLDPE 118NE | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| Staramide A40 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Hanwha Total PE P200CB | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | HDPE | Hanwha Total PE |
| Koylene ADL AS160N | Reliance Industries Limited | PP Homopolymer | Koylene ADL |
| Karina GRAY PVC COMPOUND 853-18/190-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |