TOTAL Polyethylene MDPE HT 514
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 910OQv_TOTAL-Polyethylene-MDPE-HT-514.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MDPE HT 514 is a medium density polyethylene produced by slurry loop process with hexene as co-monomer. MDPE HT 514 is a semi-high molecular weight polyethylene giving excellent mechanical properties. It shows a broad molecular weight distribution ensuring outstanding processability. MDPE HT 514 can be used alone, blended or coextruded in a wide variety of blown film applications : consumer, industrial, food or hygiene packaging. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.15 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 14 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 740 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 20 µm, blown film | 21.0 | MPa | ISO 527-3 |
| TD : Yield, 20 µm, blown film | 22.0 | MPa | ISO 527-3 |
| MD : Yield, 40 µm, blown film | 20.0 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 20.0 | MPa | ISO 527-3 |
| MD : Broken, 20 µm, blown film | 69.0 | MPa | ISO 527-3 |
| TD : Broken, 20 µm, blown film | 51.0 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 56.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 52.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 20 µm, blown film | 420 | % | ISO 527-3 |
| TD : Broken, 20 µm, blown film | 520 | % | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 530 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 620 | % | ISO 527-3 |
| Dart Drop Impact | ISO 7765-1 | ||
| 20 µm, blown film | 190 | g | ISO 7765-1 |
| 40 µm, blown film | 260 | g | ISO 7765-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 121 | °C | ISO 306 |
| Melting Temperature (DSC) | 126 | °C | ISO 3146 |
| Additional Information |
|---|
| Elmendorf, ISO 6383-2, MD, Blown Film, 20 µm: 9 N/mmElmendorf, ISO 6383-2, TD, Blown Film, 20 µm: 130 N/mmElmendorf, ISO 6383-2, MD, Blown Film, 40 µm: 17 N/mmElmendorf, ISO 6383-2, TD, Blown Film, 40 µm: 185 N/mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 190 - 220 | °C | |
| Cylinder Zone 2 Temp. | 190 - 220 | °C | |
| Cylinder Zone 3 Temp. | 190 - 220 | °C | |
| Cylinder Zone 4 Temp. | 190 - 220 | °C | |
| Cylinder Zone 5 Temp. | 190 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sevrene® 4000-40A | Vi-Chem Corporation | TPE | Sevrene® |
| HIDEN® B502 | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE | HIDEN® |
| HiFill® PPSU GY061 | Techmer Engineered Solutions | PPSU | HiFill® |
| Karina BLUE COLOR CONCENTRATE 06/183-RG-GE (CS) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 5143-88 Black 296 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |