Alpha PVC GW 3003 NATURAL LCF Q
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | AlphaGary |
| Trademark: | Alpha PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 90uLiW_Alpha-PVC-GW-3003-NATURAL-LCF-Q.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A 80°C RATED, LEAD FREE, HIGHLY FLAME RETARDED JACKETING COMPOUND. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 - 1.56 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 93 - 99 | ASTM D2240 | |
| Shaw A, 15 seconds | 86 - 92 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D412 | ||
| 0.762 mm | 18.6 | MPa | ASTM D412 |
| 1.91 mm | 16.5 | MPa | ASTM D412 |
| Tensile Elongation | ASTM D412 | ||
| Fracture, 1.91mm | 310 | % | ASTM D412 |
| Fracture, 0.762mm | 280 | % | ASTM D412 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -15.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (23°C, 100 MHz) | 3.30 | ASTM D150 | |
| Dissipation Factor (23°C, 100 MHz) | 0.019 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index (3.18 mm) | 43 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 143 | °C | |
| Cylinder Zone 2 Temp. | 154 | °C | |
| Cylinder Zone 3 Temp. | 166 | °C | |
| Cylinder Zone 4 Temp. | 171 | °C | |
| Cylinder Zone 5 Temp. | 177 | °C | |
| Adapter Temperature | 177 | °C | |
| Melt Temperature | 174 - 179 | °C | |
| Die Temperature | 177 | °C |
| Extrusion instructions |
|---|
| Melt temperature is critical, at melt temperatures above 370 degrees F it is possible to cause foaming |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® FP10KT | BASF Leuna GmbH | Nylon 6 | Miramid® |
| Sup-tech S706 | Shanghai Suptech Engineering Plastics Co. Ltd. | ABS | Sup-tech |
| Formolene® 5143S | Formosa Plastics Corporation, U.S.A. | PP Homopolymer | Formolene® |
| Generic LCP - Mineral | Generic | LCP | Generic |
| Polifor® E 20 TX/30 AS UV NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |