HiFill® PBT 1225 A
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8ydbyo_HiFill-PBT-1225-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HiFill® PBT 1225 A is a Polybutylene Terephthalate (PBT) product. It can be processed by injection molding and is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/1.05 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 2.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.080 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 57.9 | MPa | |
| Break | 53.1 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 8.0 | % | |
| Break | 50 | % | |
| Flexural Modulus | 2410 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 154 | °C | |
| 1.8 MPa, Unannealed | 54.4 | °C | |
| CLTE - Flow | 1.4E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | 16 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermylene® P7-60FG-0790 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Trexlink™ 4790 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | Trexlink™ |
| Bapolene® 122F | Bamberger Polymers, Inc. | LLDPE | Bapolene® |
| Grilamid® L 25A NZ | EMS-GRIVORY | Nylon 12 | Grilamid® |
| TOTAL Polyethylene HDPE MS 201 BN-NA (US) | TOTAL Refining & Chemicals | HDPE, HMW | TOTAL Polyethylene |