Cellidor CP 410-18
| Category: | CAP , Cellulose Acetate Propionate |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | Cellidor |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8vvm5b_Cellidor-CP-410-18.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cellidor CP 410-18 is a Cellulose Acetate Propionate (CAP) product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (210°C/2.16 kg) | 20.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/30) | 50.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1350 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 26.0 | MPa | |
| -- | 26.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 3.0 | % | |
| Break | 30 | % | |
| Flexural Modulus | 1250 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 30.0 | MPa | |
| 3.5% Strain | 30.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 35 | kJ/m² | |
| -40°C | 10 | kJ/m² | |
| -20°C | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | No Break | ||
| -40°C | No Break | ||
| -20°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 70.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 50.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 180 to 230 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ Fluoroplastic PVDF 60080001 | 3M Advanced Materials Division | PVDF | 3M™ Dyneon™ Fluoroplastic |
| Chemraz 534 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| KOPET® KP133G45BL | Kolon Plastics, Inc. | PET | KOPET® |
| Karina IVORY PVC COMPOUND 809D35/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LTP CT-1210 | Chengdu Letian Plastics Co., Ltd | PPS | LTP |