Karina BLACK PVC -E 809D48/1-C-IS-AS-LMP (034100/102-00)
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8ul4zp_Karina-BLACK-PVC--E-809D48-1-C-IS-AS-LMP-034100-102-00-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Karina BLACK PVC -E 809D48/1-C-IS-AS-LMP (034100/102-00) is a Polyvinyl Chloride product. It is available in Latin America. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.33 to 1.39 | g/cm³ | ASTM D792 |
| Cadmium Content | < 50 | ppm | ASTM D1971 |
| Chromium Content | < 100 | ppm | ASTM D1971 |
| Color | OK | ME 12 | |
| Color a | -0.770 to 0.830 | ME 12 | |
| Color b | -0.610 to 0.990 | ME 12 | |
| Color L | 25.4 to 27.0 | ME 12 | |
| Mercury Content | < 100 | ppm | ASTM D1971 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | < 100 | ppm | IEC 62321 |
| Lead Content | < 100 | ppm | ASTM D1971 |
| Maximum Variation of Elongation | < 20 | % | UL 83 |
| Maximum Variation of Tensile Strength | < 20 | % | UL 83 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 80 to 84 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | > 13.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 300 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 13.7 | MPa | UL 83 |
| Tensile Elongation 3(Break) | > 250 | % | UL 83 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -40.0 | °C | ASTM D746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+13 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 100°C |
| 3 . | Aged in Air for 168 hr at 100°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMORUN® QT99ZA | Mitsubishi Chemical Corporation | TPO (POE) | THERMORUN® |
| TUFNYL® SFM 23 FRO NATURAL | SRF Ltd. | Nylon 6 | TUFNYL® |
| Exxtral™ Performance Polyolefin HMU234 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Heraform® R3000 NAT | Radici Plastics | Acetal (POM) Copolymer | Heraform® |
| LNP™ THERMOTUF™ RF008IS compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |