Sindustris PC GP2101
| Category: | PC , Polycarbonate |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8uiYXF_Sindustris-PC-GP2101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris PC GP2101 is a Polycarbonate (PC) material filled with 10% glass fiber. It is available in Asia Pacific for injection molding. Important attributes of Sindustris PC GP2101 are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 124 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 78.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 3.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 3530 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 127 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 140 | °C | ASTM D648 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 290 to 330 | °C | |
| Nozzle Temperature | 290 to 330 | °C | |
| Processing (Melt) Temp | 300 to 340 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Back Pressure | 0.981 to 3.92 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Menzolit® MMC 1600 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| Nypol® PA A3 P5 NTLA016 NR345 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| FLEXITEQ™ F65A110 | Marplex Australia Pty. Ltd. | TPV | FLEXITEQ™ |
| Halene P M108 | Haldia Petrochemicals Ltd. | PP Homopolymer | Halene P |
| 3M™ Dyneon™ PTFE Compound PDR 05017 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |