AKROMID® C3 GF 50 1 black (4401)
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8uXRRf_AKROMID-C3-GF-50-1-black-4401-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® C3 GF 50 1 black (4401) is a 50% glass fibre reinforced, heat stabilised polyamide 6.6/6 - Blend. Applications are mainly components in mechanical engineering and the automotive industry where good flowability is required. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.57 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 65.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.2 | -- | % | |
| Flow | 0.30 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.4 | -- | % | ISO 1110 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Temperature Index | IEC 216 | |||
| 50% Loss of Tensile Strength, 20000 hr | 130 to 150 | -- | °C | |
| 50% Loss of Tensile Strength, 5000 hr | 160 to 175 | -- | °C |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 50 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16000 | 11000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 240 | 165 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.5 | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 16200 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 360 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 20 | -- | kJ/m² | |
| 23°C | 20 | 20 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 95 | 100 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 220 | -- | °C | ISO 75-2/C |
| Melting Temperature 3 | 260 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 TFE 20 SI 2 | RTP Company | Acetal (POM) Copolymer | RTP |
| STRATOR® A-3XC | EPIC Polymers | Nylon 66 | Strator® |
| Sylvin 8984-80 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Fainplast PVC CKL 0252/R | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| DOMAMID® 6G30V0A | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |