Ultramid® 8350 HS BK-102
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8taAa8_Ultramid-8350-HS-BK-102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8350 HS BK-102 is a type 6, black pigmented, impact modified graft copolymer developed for extrusion, tubing, and jacketing applications requiring a high level of toughness combined with a moderate level of flexibility. Applications Ultramid 8350 HS BK-102 is generally recommended for applications such as automotive vacuum tubing, cable jacketing, and high pressure and hydraulic hoses. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.07 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow (3.18 mm) | 1.4 | -- | % | |
| Water Absorption | ||||
| 24 hr | 1.1 | -- | % | ASTM D570 |
| 23°C, 24 hr | 1.1 | -- | % | ISO 62 |
| Saturation | 6.7 | -- | % | ASTM D570 |
| Saturated, 23°C | 6.7 | -- | % | ISO 62 |
| Balance, 50% RH | 1.9 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 1.9 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 78 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 1800 | 675 | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Yield, 23°C | 55.0 | 32.0 | MPa | ASTM D638 |
| Yield, 23°C | 52.0 | 32.0 | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Yield, 23°C | 5.0 | 9.0 | % | ASTM D638 |
| Yield, 23°C | 4.5 | 9.0 | % | ISO 527-2 |
| Fracture, 23°C | > 100 | > 100 | % | ASTM D638 |
| Nominal Tensile Strain at Break (23°C) | > 50 | > 50 | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | 1890 | -- | MPa | ASTM D790 |
| 23°C | 1600 | -- | MPa | ISO 178 |
| Flexural Strength | ||||
| 23°C | 65.0 | -- | MPa | ASTM D790 |
| 23°C | 55.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 83 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179 | |
| Notched Izod Impact | ||||
| 23°C | No Break | -- | ASTM D256, ISO 180 | |
| -40°C | 10 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 1.8 MPa, not annealed | 56.0 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 50.0 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | 1.1E-4 | -- | cm/cm/°C | ASTM E831 |
| RTI Elec | UL 746 | |||
| 1.50 mm | 65.0 | -- | °C | UL 746 |
| 3.00 mm | 65.0 | -- | °C | UL 746 |
| RTI Imp | UL 746 | |||
| 1.50 mm | 65.0 | -- | °C | UL 746 |
| 3.00 mm | 65.0 | -- | °C | UL 746 |
| RTI | UL 746 | |||
| 1.50 mm | 65.0 | -- | °C | UL 746 |
| 3.00 mm | 65.0 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | > 1.0E+13 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.50 mm | HB | -- | UL 94 | |
| 3.00 mm | HB | -- | UL 94 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Cylinder Zone 1 Temp. | 245 - 260 | °C | |
| Cylinder Zone 3 Temp. | 240 - 255 | °C | |
| Cylinder Zone 5 Temp. | 240 - 250 | °C | |
| Flange temperature | 225 - 240 | °C | |
| Head Temperature | 225 - 245 | °C | |
| Extruder Screw L/D Ratio | 20.0:1 to 24.0:1.0 | ||
| Extruder Screw Compression Ratio | 3.5:1.0 to 4.0:1.0 | ||
| Melt Temperature | 240 - 250 | °C | |
| Die Temperature | 225 - 240 | °C |
| Extrusion instructions |
|---|
| Screw Parameters Metering Section : 40% Transition Section : 6 to 7 flights Feed Section : balance of screw length |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J-3000GP | Prime Polymer Co., Ltd. | PP Homopolymer | Prime Polypro™ |
| Monprene® RG-20180 X (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| Generic TP, Unspecified | Generic | TP, Unspecified | Generic |
| Eltex® B4020P | INEOS Olefins & Polymers Europe | HDPE Copolymer | Eltex® |
| KEBAFLEX® U A 85 HT B01 natural | BARLOG plastics GmbH | TPU, Unspecified | KEBAFLEX® |