Tempalux® Medical
| Category: | PEI , Polyether Imide |
| Manufacturer: | Westlake Plastics Company |
| Trademark: | Tempalux® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8sqaHo_Tempalux-Medical.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Medical grade Tempalux is made from Ultem® polyetherimide resin, an amorphous thermoplastic which exhibits excellent resistance to a wide range of chemicals and disinfectants. Ultem maintains its size and shape over a broad temperature range as well as tolerates a high amount of stress over extended periods of time. Recommended sterilization techniques for Tempalux include EtO gas, radiation, steam autoclaving, dry heat and cold sterilization. Applications Include:
Advantages of Medical Grade Tempalux:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2960 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 105 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | |
| Break | 60 | % | |
| Flexural Modulus | 3310 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 152 | MPa | ASTM D790 |
| Compressive Modulus | 3310 | MPa | ASTM D695 |
| Compressive Strength | 151 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact | 1300 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 210 | °C | |
| 1.8 MPa, Unannealed | 200 | °C | |
| CLTE - Flow | 5.6E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.406 mm | V-0 | ||
| 1.91 mm | 5VA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® Fine Powders T GREY 5161 MAC | Arkema | Nylon 11 | Rilsan® Fine Powders |
| SynPlast™ DOA-FM | PolyOne Corporation | Di (2-ethylhexyl) Adipate | SynPlast™ |
| TOTAL Polypropylene PPH 3622 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Varcum 29440 | Durez Corporation | Phenolic | Varcum |
| Plexiglas® Satinice df22 zk6BR | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |