MAJORIS MA201T
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8sT4Kd_MAJORIS-MA201T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MA201T is a 20% mineral reinforced, PP compound intended for extrusion.. APPLICATIONS MA201T is recommended for the extrusion of profiles (building, electrical, furniture and construction profiles or pipes). Products made from this material show a high dimensional stability and low process shrinkage. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.50 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 26.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 1800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 49 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 105 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 9.0 | hr | |
| Cylinder Zone 1 Temp. | 190 to 230 | °C | |
| Cylinder Zone 3 Temp. | 190 to 230 | °C | |
| Cylinder Zone 5 Temp. | 190 to 230 | °C | |
| Melt Temperature | 200 to 230 | °C | |
| Head Temperature | 200 to 230 | °C | |
| Die Temperature | 200 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® PVC VSS-F120 | Sumitomo Bakelite Co., Ltd. | PVC, Unspecified | SUMILITE® PVC |
| Alpha PVC GW 2409-VW1 NAT 50 LCF | AlphaGary | PVC, Semi-Rigid | Alpha PVC |
| Exxtral™ Performance Polyolefin BMU130 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Karina BLUE PVC COMPOUND 360-06/858-IS-SD (FREE) (***) | Karina Ind. e Com. de Plásticos Ltda | Polyolefin, Unspecified | Karina |
| LUBEMID B27 CM30 NATURAL | LUBEN PLAST srl | Nylon 6 | LUBEMID |