3M™ Dyneon™ Fluoroelastomer FE 5624Q

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ Fluoroelastomer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	8r9uXv_3MDyneonFluoroelastomerFE5624Q.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
3M™ Dyneon™ Fluoroelastomer FE 5624Q is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FE 5624Q has an incorporated bisphenol cure system. Special Features Composition: dipolymer of vinylidene fluoride and hexafluoropropylene Proprietary incorporated cure technology Process targets: injection and transfer moulding, extrusion and calendering Excellent mould release - can be used in automated injection moulding equipment Fast curing version of 3M™ Dyneon™ Fluoroelastomer FE 5620Q Improved cure technology helps promote more consistent part size from successive moulding cycles Improved scorch resistance at high moulding temperatures Clean running Compounds prepared from Dyneon FE 5624Q can be formulated to meet Mil-R-83248 Typical Applications 3M™ Dyneon™ Fluoroelastomer FE 5624Q is suitable for usage in injection moulding (e.g. production of O-rings) and extrusion applications.

Message

3M™ Dyneon™ Fluoroelastomer FE 5624Q is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FE 5624Q has an incorporated bisphenol cure system.

Special Features

Composition: dipolymer of vinylidene fluoride and hexafluoropropylene

Proprietary incorporated cure technology

Process targets: injection and transfer moulding, extrusion and calendering

Excellent mould release - can be used in automated injection moulding equipment

Fast curing version of 3M™ Dyneon™ Fluoroelastomer FE 5620Q

Improved cure technology helps promote more consistent part size from successive moulding cycles

Improved scorch resistance at high moulding temperatures

Clean running

Compounds prepared from Dyneon FE 5624Q can be formulated to meet Mil-R-83248

Typical Applications
3M™ Dyneon™ Fluoroelastomer FE 5624Q is suitable for usage in injection moulding (e.g. production of O-rings) and extrusion applications.

General Information
Features	Fast curing Good demoulding performance
Uses	O-rings
Agency Ratings	MIL R-83248
Appearance	Opacity White-like
Forms	Thick sheet
Processing Method	Extrusion Resin transfer molding Calendering Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.80	g/cm³	Internal method
Mooney Viscosity (ML 1+10, 121°C)	29	MU	Internal method
Fluorine Content	66	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	78		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(100% Strain)	6.50	MPa	ASTM D412A
Tensile Strength ²	15.4	MPa	ASTM D412A
Tensile Elongation ³(Break)	210	%	ASTM D412A
Compression Set			ASTM D1414
200°C, 70 hr ⁴	20	%	ASTM D1414
200°C, 70 hr ⁵	15	%	ASTM D1414

Note Message
1 .	D mould
2 .	Die D
3 .	D mould
4 .	Post cured 16 hours @ 230°C
5 .	Post cured 24 hours @ 260°C

Resin Grade	Manufacturer	Category	Trademark
RTP 205 A TFE 13 SI 2	RTP Company	Nylon 6	RTP
TEKAFIN™ P730HG	Mando Advanced Materials Co., Ltd.	PP, Unspecified	TEKAFIN™
VESTAMID® L L2124	Evonik Industries AG	Nylon 12	VESTAMID® L
Zytel® FR50 NC010A	DuPont Performance Polymers	Nylon 66	Zytel®
KARIPRENE NATUR. -E 5525/ 1-TRE	Karina Ind. e Com. de Plásticos Ltda	TPE	KARIPRENE