TARFLON™ #1700
| Category: | PC , Polycarbonate |
| Manufacturer: | Formosa Idemitsu Petrochemical Corporation |
| Trademark: | TARFLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8qMNTo_TARFLON1700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Grades
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 27.0 | cm³/10min | ISO 1133 |
| Spiral Flow | 25.0 | cm | Internal method |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction : 2.00mm | 0.50 - 0.70 | % | Internal method |
| Flow direction : 2.00mm | 0.50 - 0.70 | % | Internal method |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.23 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ISO 2039-2 | ||
| M scale | 50 | ISO 2039-2 | |
| R scale | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 65.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 95 | % | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 40 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 125 | °C | ISO 75-2/A |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec (0.360 mm) | 130 | °C | UL 746 |
| RTI Imp (0.360 mm) | 125 | °C | UL 746 |
| RTI (0.360 mm) | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 30 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 2.85 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 9.2E-3 | IEC 60250 | |
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.400 to mm) | V-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 85.0 - 89.0 | % | ISO 13468-1 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | >PC |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 5.0 - 8.0 | hr | |
| Rear Temperature | 260 - 300 | °C | |
| Middle Temperature | 260 - 300 | °C | |
| Front Temperature | 260 - 300 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 24h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4003 A | RTP Company | PPA | RTP |
| Telcar® GS7033 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| Sylvin 8200-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Delas 195 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PVC+NBR | Delas |
| Sylvin 86032-90 Clear 8443 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |