SABIC® PPcompound 95610CSU10
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8q9qUE_SABIC-PPcompound-95610CSU10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 95610CSU10 is a mineral filled modified polypropylene. SABIC® PPcompound 95610CSU10 is a material with a high impact and stiffness. The material is part of the SABIC®PP CS systems ans also available as a CS system: using a mixture of 80% SABIC®PP 95610 and 20% SABIC®PPcompound 20MBTFU yields similar properties as listed below. SABIC®PPcompound 95610CSU10 is a designated auto grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.961 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.4 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 1.2 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 59 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 17.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 19.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 700 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 1100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 10 | kJ/m² | |
| 0°C, Injection Molded | No Break | ||
| 23°C, Injection Molded | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 80.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 120 | °C | ISO 306/A |
| CLTE - Flow (23 to 80°C) | 1.1E-4 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ALE-93A-B20 | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| Tisakril® ABS UNR FR | Tisan | ABS | Tisakril® |
| Diofan® A 297 | Solvay Specialty Polymers | PVDC | Diofan® |
| Lutene® H BE0350 | LG Chem Ltd. | HDPE | Lutene® H |
| Polidiemme® G/440 | Solvay Specialty Polymers | TSE | Polidiemme® |