Duratron® T4503

Category:	PAI , Polyamide-imide
Manufacturer:	Quadrant Engineering Plastic Products
Trademark:	Duratron®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	8obOr8_Duratron-T4503.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Duratron® T4503 compression molded PAI is commonly used for dies and patterns of formed metal parts, or as thermal insulators and isolators. It is similar in composition to Duratron® T4203 PAI, and selected when larger shapes are required.

Duratron® PAI is the highest performing melt processable plastic. It has superior resistance to elevated temperatures. It is capable of performing under severe stress conditions at continuous temperatures to 500°F (260°C). Parts machined from Duratron® PAI stock shapes provide greater compressive strength and higher impact resistance than most advanced engineering plastics. Its extremely low coefficient of linear thermal expansion and high creep resistance deliver excellent dimensional stability over its entire use range. Duratron® PAI is an amorphous material with a Tg (glass transition temperature) of 537°F (280°C).

Data provided by Quadrant Engineering Plastic Products from tests on stock shapes and parts produced by Quadrant EPP.

General Information
Features	Acid Resistant Alcohol Resistant Amorphous Good Chemical Resistance Good Compressive Strength Good Creep Resistance Good Dimensional Stability Good Stiffness Good Thermal Stability Good Wear Resistance High Impact Resistance High Strength Hydrocarbon Resistant Solvent Resistant
Uses	Insulation Shield
Forms	Customizable Forms Preformed Parts Rod Tubing
Processing Method	Compression Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.40	g/cm³	ASTM D792
Water Absorption			ASTM D570
24 hr	0.35	%
Saturation	1.7	%

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness			ASTM D785
E-Scale	80
M-Scale	119
Durometer Hardness (Shore D)	90		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3450	MPa	ASTM D638
Tensile Strength (Ultimate)	124	MPa	ASTM D638
Tensile Elongation (Break)	5.0	%	ASTM D638
Flexural Modulus	4140	MPa	ASTM D790
Flexural Strength (Yield)	165	MPa	ASTM D790
Compressive Modulus	2410	MPa	ASTM D695
Compressive Strength (10% Strain)	124	MPa	ASTM D695
Coefficient of Friction (vs. Steel - Static)	0.30		Internal Method
Wear Factor	2000	10^-8 mm³/N·m	ASTM D3702

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	80	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	278	°C	ASTM D648
Maximum Use Temperature - Long Term, Air	260	°C

Additional Information	Nominal Value	Unit	Test Method
Limiting Pressure Velocity ¹	0.263	MPa·m/s	Internal Method

Thermal	Nominal Value	Unit	Test Method
Glass Transition Temperature	275	°C	ASTM D3418
CLTE - Flow ²(-40 to 149°C)	2.7E-5	cm/cm/°C	ASTM E831
Thermal Conductivity	0.26	W/m/K	ASTM F433

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity ³	> 1.0E+13	ohms	Internal Method
Dielectric Strength ⁴	24	kV/mm	ASTM D149
Dielectric Constant (1 MHz)	4.20		ASTM D150
Dissipation Factor (1 MHz)	0.031		ASTM D150

Flammability	Nominal Value	Unit	Test Method
Flame Rating (3.18 mm, Estimated Rating)	V-0		UL 94

Note Message
1 .	4:1 safety factor
2 .	68°F
3 .	EOS/ESD S11.11
4 .	Method A (Short-Time)

Resin Grade	Manufacturer	Category	Trademark
RTP 103 AV (Solid)	RTP Company	PP, Unspecified	RTP
Spartech PS SP-2010	Spartech Plastics	PS (HIPS)	Spartech
APEX® RE 8018	Teknor Apex Company	PVC, Rigid	APEX®
Delrin® 100 NC010	DuPont Performance Polymers	Acetal (POM) Homopolymer	Delrin®
Hostacom ERC 361N NAT	LyondellBasell Industries	PP Copolymer	Hostacom