LIHAN® CT9000
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Nanjing Lihan Chemical Co., Ltd. |
| Trademark: | LIHAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8oUW5r_LIHAN-CT9000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fire resistance PC/PBT alloy Pamphleti The P0lycarbonate(PC) material has good impact strength, surface glossiness and self-extinguishing, but its fluidity and anti—environmental stress are very poor. The Polyethylene terephthalate (PBT) has good processability and electrical property. The PC/PBT alloy has both advantages rolled into one. High fire resistant PC/PBT alloy has reached UL-94 V-0(O.8mm) and 5VA(2.5mm), and it satisfies the European Commission ROHS. The material has been recognized by multinational electronics operation and listed as one of the company global purchase items. The material can be used to electronic parts, apparatus shell. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.70 to 0.90 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 25 | % | ISO 527-2 |
| Flexural Modulus | 2100 | MPa | ISO 178 |
| Flexural Stress | 70.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 78.0 | °C | ISO 75-2/A |
| Melting Temperature | 220 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 2.50 mm | 5VA |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 240 to 265 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® PA 1408 | Premix Oy | Nylon 6 | PRE-ELEC® |
| Tenite™ Acetate 105E3V36327 Clear, Trsp | Eastman Chemical Company | CA | Tenite™ Acetate |
| TPV Elastoprene® N50D-E | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| Greenflex® FD 20 F | Versalis S.p.A. | EVA | Greenflex® |
| Perfactory® Easy Cast EC500 | EnvisionTEC, Inc. | Unspecified | Perfactory® |