Pibiter® NRV220AE NAT001
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Pibiter® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8oGkyn_Pibiter-NRV220AE-NAT001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% glass fiber reinforced, flame retardant PBT grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.50 | % | Internal Method |
| Water Absorption | |||
| 23°C, 24 hr | 0.045 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.30 | % | ISO 62 |
| Ash Content | 20 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ASTM D638 |
| Tensile Strength (Break) | 102 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 7500 | MPa | ASTM D790 |
| Flexural Strength | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 222 | °C | |
| 1.8 MPa, Unannealed | 209 | °C | |
| Vicat Softening Temperature | 205 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 235 | °C | |
| Middle Temperature | 245 | °C | |
| Front Temperature | 250 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TABOND 5009 | SILON s.ro | PP Copolymer | TABOND |
| Tritan™ LX151HF | Eastman Chemical Company | Copolyester | Tritan™ |
| Vydyne® R515J NT0689 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Generic PP, Unspecified - Glass Bead | Generic | PP, Unspecified | Generic |
| LNP™ THERMOCOMP™ 9X99089 compound | SABIC Innovative Plastics Europe | PEI | LNP™ THERMOCOMP™ |