SURPASS® HPs900-C
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | NOVA Chemicals |
| Trademark: | SURPASS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8nSSdc_SURPASS-HPs900-C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SURPASS® HPs900-C is a Linear Low Density Polyethylene material. It is available in North America for coextrusion or film extrusion. Important attributes of SURPASS® HPs900-C are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.917 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 25 µm, Blown Film | 135 | MPa | |
| 1% Secant, TD : 25 µm, Blown Film | 155 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 25 µm, Blown Film | 9.00 | MPa | |
| TD : Yield, 25 µm, Blown Film | 9.00 | MPa | |
| MD : Break, 25 µm, Blown Film | 49.0 | MPa | |
| TD : Break, 25 µm, Blown Film | 43.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm, Blown Film | 520 | % | |
| TD : Break, 25 µm, Blown Film | 750 | % | |
| Dart Drop Impact (25 µm, Blown Film) | 460 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, Blown Film | 280 | g | |
| TD : 25 µm, Blown Film | 450 | g | |
| Seal Initiation Temperature (25 µm, Blown Film) | 100 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm, Blown Film) | 79 | ASTM D2457 | |
| Haze (25.0 µm, Blown Film) | 4.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Low Friction Puncture - Blown Film (25.0 µm) | 840 | J/cm | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STABAMID® 26 FS 1 | Solvay Polyamide & Intermediates | Nylon 66 | STABAMID® |
| UNIGARD™ RE DFDA-1980 NT | The Dow Chemical Company | TP, Unspecified | UNIGARD™ |
| Elastron® V V100.A73.N | Elastron USA, Inc. | TPV | Elastron® V |
| EMLON® 66 MTF 20 FR V2 | EMAS Plastik San.Tic.AS. | Nylon 66 | EMLON® |
| INCOLOR PEUV BK003 | Infinity LTL Engineered Compounds | HDPE | INCOLOR |