Electrafil® ABS 03011 BK MB
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8kxbri_Electrafil-ABS-03011-BK-MB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Electrafil® ABS 03011 BK MB is an Acrylonitrile Butadiene Styrene (ABS) product filled with filler. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.28 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 48.3 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 3310 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 240 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 102 | °C | |
| 1.8 MPa, Unannealed | 96.1 | °C | |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0 to 1.0E+2 | ohms | ASTM D257 |
| Volume Resistivity | 1.0 to 1.0E+2 | ohms·cm | ASTM D257 |
| Shielding Effectiveness 1 | 55 | dB | ASTM D149 |
| Static Decay | < 0.1 | sec | FTMS 101B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 to 87.8 | °C | |
| Drying Time | 2.0 to 16 | hr | |
| Rear Temperature | 216 to 232 | °C | |
| Middle Temperature | 221 to 238 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Nozzle Temperature | 199 to 221 | °C | |
| Processing (Melt) Temp | 232 to 260 | °C | |
| Mold Temperature | 71.1 to 87.8 | °C |
| Note Message | |
|---|---|
| 1 . | 30 to 1000 MHz |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXALEN™ PPH305G30 | SAX Polymers | PP Homopolymer | SAXALEN™ |
| SHIN-A SEY-175APM75 | SHIN-A T&C | Epoxy | SHIN-A |
| Karina BLACK PVC COMPOUND -E 650D48/ 1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOTUF™ RF006I compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |
| Braskem PE GE7252XP | Braskem | HDPE | Braskem PE |