ALCOM® LD2 PC 1000 14008 WT1009-14
| Category: | PC , Polycarbonate |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALCOM® LD2 PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8kDdtg_ALCOM-LD2-PC-1000-14008-WT1009-14.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCOM® LD2 PC 1000 14008 WT1009-14 is a Polycarbonate (PC) product filled with filler. It is available in Asia Pacific, Europe, or North America. Applications of ALCOM® LD2 PC 1000 14008 WT1009-14 include automotive and lighting applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 20.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 66.0 | MPa | |
| -- | 66.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 6.0 | % | |
| Break | 70 | % | |
| Flexural Modulus | 2450 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 100 | MPa | |
| 3.5% Strain | 76.0 | MPa | |
| Flexural Deflection at Max Force | 7.0 | % | ISO 178 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fire Performance (1.00 mm) | passed | FMVSS 302 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Half Power Angle 1(1.00 mm) | 59.0 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 12 | kJ/m² | |
| -40°C | 12 | kJ/m² | |
| -20°C | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | No Break | ||
| -40°C | No Break | ||
| -20°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 124 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 142 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 0.750 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 850 | °C | |
| 2.00 mm | 850 | °C | |
| 3.00 mm | 960 850 | °C | |
| 4.00 mm | 960 850 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance 2(Total, 1000 µm) | 12.0 | % | ISO 13468 |
| Haze 3(1000 µm) | 95 | % | ISO 13468 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 100 to 120 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 270 to 310 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | A, 2° |
| 2 . | A, 2° |
| 3 . | Ill. A, 2° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2185 | RTP Company | PEI | RTP |
| SLOVALEN® PH 99 GB 30 LS | Plastcom | PP, Unspecified | SLOVALEN® |
| Karina WHITE PVC COMPOUND -E 854-10/150-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYfill PPH TS3020 | Polykemi AB | PP Homopolymer | POLYfill |
| Sylvin 5210-75 Orange 5106 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |