Ravathane R210A90UV
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | RAVAGO Kimya Plastik Sanayi ve Ticaret A.S. |
| Trademark: | Ravathane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8i7onR_Ravathane-R210A90UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: Product is based on standard grade polyether and has strong resilience and tear resistance, excellent abrasion resistance, excellent resistance to hydrolysis failure and microbial attack, good stability towards solvents and light. Application: Injection molding and extrusion |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 91 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Resistance | 35.0 | mm³ | ISO 4649 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Extruder Screw L/D Ratio | 25:1 | ||
| Screw cooling | Air |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| 100% strain | 8.00 | MPa | ISO 37 |
| 300% strain | 18.0 | MPa | ISO 37 |
| Tensile Stress (Yield) | 42.0 | MPa | ISO 37 |
| Tensile Elongation (Break) | 550 | % | ISO 37 |
| Tear Strength 1 | 120 | kN/m | ISO 34-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Rear Temperature | 195 | °C | |
| Middle Temperature | 205 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 205 | °C | |
| Injection Pressure | 70.0 | MPa |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 200 - 210 | °C | |
| Cylinder Zone 2 Temp. | 215 - 225 | °C | |
| Cylinder Zone 3 Temp. | 230 - 240 | °C | |
| Cylinder Zone 4 Temp. | 200 - 210 | °C | |
| Die Temperature | 200 - 210 | °C |
| Extrusion instructions |
|---|
| Type: 30/25d, Screw: 3:1, Speed: 3:1, Speed: 50 rpm, Thickness Die: 0.2mm, Pre-heating: 1h@105°C |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoPrene 67A-1000 | KMI Group Inc. | TPV | PrimoPrene |
| Comai 721-1 NT | Comai Ltda | PP, Unspecified | Comai |
| Elastocon® 8088N | Elastocon TPE Technologies | TPE | Elastocon® |
| LITEN RL 58 UV | UNIPETROL RPA | LPE Copolymer | LITEN |
| Karina GREEN PVC COMPOUND 902-40/485-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |