LNP™ LUBRICOMP™ Lexan_LF1520A compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8hlK5E_LNP-LUBRICOMP-Lexan-LF1520A-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP LEXAN_LF1520A compound is a 20% glass reinforced, 15% PTFE filled PC. Flame retardant and wear resistant. Tight tolerances. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.15 to 0.25 | % | |
| Across Flow : 3.20 mm | 0.20 to 0.45 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 93.1 | MPa | |
| Break | 93.1 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 5.0 | % | |
| Break | 5.0 | % | |
| Flexural Modulus 3(50.0 mm Span) | 6210 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 148 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 530 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 17.6 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 133 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 128 | °C | |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.2E-5 | cm/cm/°C | |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 5 | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 266 to 288 | °C | |
| Middle Temperature | 277 to 299 | °C | |
| Front Temperature | 288 to 310 | °C | |
| Nozzle Temperature | 282 to 304 | °C | |
| Processing (Melt) Temp | 288 to 310 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Akestra™ 100 | Perstorp Holding AB | Copolyester | Akestra™ |
| DELPET™ SRB100 | Asahi Kasei Chemicals Corporation | Acrylic (PMMA) | DELPET™ |
| EPDM 565 | The Dow Chemical Company | EPDM | EPDM |
| Karina CLEAR PVC COMPOUND 75/202 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Durethan® B 38 FKA 000000 | LANXESS GmbH | Nylon 6 | Durethan® |