DOMAMID® A1-002-V15-N
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DOMO Engineering Plastics GmbH |
| Trademark: | DOMAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8ghMkL_DOMAMID-A1-002-V15-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6, medium viscosity, 15% glass fiber reinforced, natural |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 60.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 23°C, 72 hr | 0.95 | % | |
| Flow : 23°C, 72 hr | 0.45 | % | |
| Water Absorption 2 | ISO 62 | ||
| Saturation, 23°C | 2.2 | % | |
| Equilibrium, 23°C, 50% RH | 0.30 | % | |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 145 | cm³/g | ISO 307 |
| Ash Content (650°C) | 15 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 190 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 125 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.7 | % | ISO 527-2/1A/5 |
| Flexural Modulus 3 | 4540 | MPa | ISO 178 |
| Flexural Stress 4 | 197 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 6.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 48 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 207 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 175 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 215 | °C | ISO 306/A50 |
| -- | 210 | °C | ISO 306/B50 |
| Melting Temperature | 221 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | VDE 0303-3 |
| Volume Resistivity | 1.0E+15 | ohms·cm | VDE 0303-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 5(2.00 mm) | 42 | mm/min | ISO 3795 |
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | VDE 0471/2 |
| Note Message | |
|---|---|
| 1 . | 50%RH, between 16 to 72 hrs |
| 2 . | 24 hrs |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | FMVSS302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Andur 6500 DPLF/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| BONDYRAM® TL 3101B | Polyram Ram-On Industries | PE, Unspecified | BONDYRAM® |
| DURACON® GH-25LV | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| Lucent PBT GPB-130L | Lucent Polymers, Inc. | PBT | Lucent PBT |
| Sumiliteresin® PR-51618 BI | SBHPP | Phenolic | Sumiliteresin® |