Alkatuff® 601
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Qenos Pty Ltd |
| Trademark: | Alkatuff® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8gDXWx_Alkatuff-601.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
601 is a hexene copolymer linear low density polyethylene, designed for a variety of film applications. 601 is formulated with antiblock, stabilisation and slip (high slip) additives. 601 is intended for general purpose applications such as liners, garbage, industrial and agricultural films. 601 is not recommended for use in outdoor applications (especially applications where there may be prolonged exposure to sunlight, eg. agricultural films) without the addition of appropriate Hindered Amine based Light Stabilisers (HALS). 601 is suitable for food contact applications and conforms to the requirements of the United States Food and Drug Administration CFR 21 177.1520, paragraph (c), item 3.1. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.13 0.15 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 28 50 | µm | |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 28 µm | 210 | MPa | ASTM D882 |
| 2% secant, MD : 50 µm | 220 | MPa | ASTM D882 |
| 2% secant, TD : 28 µm | 220 | MPa | ASTM D882 |
| 2% secant, TD : 50 µm | 240 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 28 µm | 9.00 | MPa | ASTM D882 |
| MD : Yield, 50 µm | 10.0 | MPa | ASTM D882 |
| TD : Yield, 28 µm | 12.0 | MPa | ASTM D882 |
| TD : Yield, 50 µm | 12.0 | MPa | ASTM D882 |
| MD : Broken, 28 µm | 28.0 | MPa | ASTM D882 |
| MD : Break, 50 µm | 34.0 | MPa | ASTM D882 |
| TD : Broken, 28 µm | 24.0 | MPa | ASTM D882 |
| TD : Break, 50 µm | 30.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 28 µm | 750 | % | ASTM D882 |
| MD : Break, 50 µm | 1000 | % | ASTM D882 |
| TD : Broken, 28 µm | 800 | % | ASTM D882 |
| TD : Break, 50 µm | 1000 | % | ASTM D882 |
| Dart Drop Impact | ASTM D1709 | ||
| 28 µm, blown film | 130 | g | ASTM D1709 |
| 50 µm, blown film | 240 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 28 µm | 310 | g | ASTM D1922 |
| MD : 50 µm | 590 | g | ASTM D1922 |
| TD : 28 µm | 510 | g | ASTM D1922 |
| TD : 50 µm | 980 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 28.0 µm, blown film | 72 | ASTM D2457 | |
| 50.0 µm, blown film | 74 | ASTM D2457 | |
| Haze | ASTM D1003 | ||
| 28.0 µm, blown film | 8.0 | % | ASTM D1003 |
| 50.0 µm, blown film | 10 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from blown film processed at a blow up ratio of 3.5:1. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 400 | RTP Company | PS (GPPS) | RTP |
| Sipolprene® 55200 W | SIPOL S.p.A | TPC-ET | Sipolprene® |
| LG PS 15NFI | LG Chem Ltd. | PS (GPPS) | LG PS |
| MAJ'ECO EN030LA | AD majoris | Biodeg Polymers | MAJ'ECO |
| PLUSTEK PA700BL10 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |