Starflam AFR200B
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starflam |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8fcDnV_Starflam-AFR200B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starflam AFR200B is a Unfilled, Flame Retardant Polyamide 66 Injection Molding Resin |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 1.0 to 1.5 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 6.5 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 80.0 | MPa | |
| Break | 80.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 3.7 | % | |
| Break | 6.0 | % | |
| Flexural Modulus 2 | 2800 | MPa | ISO 178 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3 | ISO 180/1A | ||
| -40°C | 3.0 | kJ/m² | |
| -20°C | 4.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 216 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 100 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 245 | °C | ISO 306/B120 |
| Ball Pressure Test 5(125°C) | Pass | IEC 60695-10-2 | |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 8.5E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 8.5E-5 | cm/cm/°C | |
| RTI Elec | 65.0 | °C | UL 746 |
| RTI Imp | 65.0 | °C | UL 746 |
| RTI Str | 65.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | IEC 60112 | ||
| -- | 350 | V | |
| Solution B | 250 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Oxygen Index | 29 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Processing (Melt) Temp | 270 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 120*10*4 |
| 5 . | 125°C ±2°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® CP 1804T | Plastic Solutions, Inc. | PP Impact Copolymer | PrimaFlex® |
| Teflon® PTFE 62XT X | DuPont Fluoropolymers | PTFE | Teflon® PTFE |
| Desmopan® DP 2586A | Covestro - PUR | TPU-Polyester | Desmopan® |
| Ferro PP LPP40BC93HB WHITE | Ferro Corporation | PP Homopolymer | Ferro PP |
| IDI STC 3142A | IDI Composites International | Vinyl Ester | IDI STC |