Order Products : sales@su-jiao.com
ELEVATE™ EF563
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | ELEVATE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8fPo5y_ELEVATE-EF563.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake EF563 is 6.5% ethylene vinyl acetate copolymer designed for blown film extrusion. EF563 has excellent drawdown, low temperature melting/ dispersion, and clarity optics in a soft but very tough film. Application/Uses: Batch Inclusion bags Film packaging |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.932 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 1.1 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 6.5 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 38 µm, blown film | 96.5 | MPa | ASTM D882 |
| 1% secant, TD : 38 µm, blown film | 103 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 38 µm, blown film | 31.0 | MPa | ASTM D882 |
| TD : Broken, 38 µm, blown film | 22.8 | MPa | ASTM D882 |
| Dart Drop Impact (38 µm, Blown Film) | 180 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 103 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 1(45°, 38.1 µm, Blown Film) | 60 | ASTM D2457 | |
| Haze 2(38.1 µm, Blown Film) | 10 | % | ASTM D1003 |
| Additional Information |
|---|
| Typical film properties as measured on 1.5 mil blown film fabricated with a 35 mil die gap, 2.5:1 BUR, 400 F melt temperature, and 50 F chilled air at 7 lbs/hr/die in rate. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 193 - 204 | °C |
| Note Message | |
|---|---|
| 1 . | Based on LV formulation - contains 1200 ppm erucamide slip and 9000 ppm antiblock. |
| 2 . | Based on LV formulation - contains 1200 ppm erucamide slip and 9000 ppm antiblock. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PE PB-681 | Braskem | LDPE | Braskem PE |
| LNP™ THERMOCOMP™ DF00A8P compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |
| LinGen FR350 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TEEE | LinGen |
| LEXAN™ EXL9132 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Novalloy-A A2706 | PlastxWorld Inc. | ABS+Nylon | Novalloy-A |