Braskem PE SLH218
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8ervIV_Braskem-PE-SLH218.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SLH218 is a LLDPE Hexene copolymer produced by Braskem. It shows a good balance between optical properties, mechanical properties (Mainly stretchability), sealability and processability. Very low gel contained. The minimum biobased content of this grade is 84%, determined according to ASTM D6866. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.916 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.3 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture, 38 µm, extruded film | 40.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm, extruded film | 40.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm, extruded film | 1200 | % | ASTM D882 |
| TD : Fracture, 38 µm, extruded film | 1500 | % | ASTM D882 |
| Flexural Modulus | ASTM D882 | ||
| 1% Secant, MD : 38 µm, Cast Film | 210 | MPa | ASTM D882 |
| 1% Secant, TD : 38 µm, Cast Film | 240 | MPa | ASTM D882 |
| Dart Drop Impact (38 µm, Cast Film) | 110 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm, cast film | 240 | g | ASTM D1922 |
| TD : 38 µm, cast film | 520 | g | ASTM D1922 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Biobased Content | > 84 | % | ASTM D6866 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 250 | °C |
| Extrusion instructions |
|---|
| Screen Package: 40/40 - 100% pure; 40/60/40 - BlendMass Temperature: 230°C (max 260°C) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymist® XPP 527 | Solvay Specialty Polymers | PTFE | Polymist® |
| SABIC® LLDPE 118N | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| TEREZ PA 6.6 7600 H | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| BONDYRAM® TL1306 | Polyram Ram-On Industries | PP, Unspecified | BONDYRAM® |
| FILLMA 5002F30C | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | FILLMA |