INEOS LLDPE LL6910KJ
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8eo7IS_INEOS-LLDPE-LL6910KJ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LLDPE film products Applications LL6910KJ is particularly suitable for use in lean and rich blend blown film applications, such as overwrap, counter bags, shrink film (lean blends, 10 to 30% LLDPE) and stand-up pouch applications. Benefits and Features LL6910KJ is a linear low density polyethylene copolymer containing hexene-1 as the co-monomer. It offers the following properties:
LL6910KJ gives high slip film with easy opening properties when used pure in the thickness range 30 - 70 µm. Addition of other polymers, masterbatches and pigments, or use of other thicknesses may alter film slip and antiblock performance. If corona treatment is necessary, the level should normally be in the range 38-48 mN/m. We recommend that you consult your INEOS technical representative for further advice on the use of LL6910KJ. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.937 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.23 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Tensile Modulus - 1% Secant (38 µm, Blown Film) | 450 | MPa | ISO 1184 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 38 µm, blown film | 18.0 | MPa | ISO 527-3 |
| TD : Yield, 38 µm, blown film | 21.0 | MPa | ISO 527-3 |
| MD : 38 µm, blown film | 54.0 | MPa | ISO 527-3 |
| TD : 38 µm, blown film | 36.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 1184 | ||
| MD : Broken, 38 µm, blown film | 780 | % | ISO 1184 |
| TD : Broken, 38 µm, blown film | 990 | % | ISO 1184 |
| Dart Drop Impact (38 µm, Blown Film) | 65 | g | ASTM D1709A |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 38.0 µm | 13.7 | kN/m | ASTM D1922 |
| TD : 38.0 µm | 127.5 | kN/m | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 121 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 38.0 µm, Blown Film) | 50 | ASTM D2457 | |
| Haze (38.0 µm, Blown Film) | 15 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 38 µm film, 2:1 blow up ratio, 230°C melt temperature. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Synthos PS GP 535 | Synthos S.A. | PS (GPPS) | Synthos PS |
| DAI-EL™ G-671 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| Generic Nylon 11 - Glass Fiber | Generic | Nylon 11 | Generic |
| ELASTOSIL® R 770/60 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| PermaStat® 202 A | RTP Company | Nylon 6 | PermaStat® |