Multi-Pro® 2505 CU
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Multibase, A Dow Corning Company |
| Trademark: | Multi-Pro® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8dpR29_Multi-Pro-2505-CU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Multi-Pro® 2505 CU is a Polypropylene product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive. Primary characteristic: good uv resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 26.5 | MPa | ISO 527-2 |
| Flexural Modulus | 1780 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 4.3 | kJ/m² | ISO 180 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 199 | °C | |
| Middle Temperature | 216 | °C | |
| Front Temperature | 221 | °C | |
| Nozzle Temperature | 227 | °C | |
| Processing (Melt) Temp | 227 | °C | |
| Mold Temperature | 26.7 to 48.9 | °C | |
| Injection Rate | Moderate-Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TechnoDur PBT-PET GF15 black (9970) | TechnoCompound GmbH | PBT+PET | TechnoDur |
| TEREZ PA 6.6 7500 GF 35 HY | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Delta ATR-2G50 | Delta Polymers | Acetal (POM) Copolymer | Delta |
| Flontech® FT-CARR15-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| ESENTTIA 20C65NA | Polipropileno del Caribe S.A. | PP Impact Copolymer | ESENTTIA |