ALCOM® PC 740/4 GY1227-08LD
| Category: | PC , Polycarbonate |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALCOM® PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8bfgOM_ALCOMPC7404GY122708LD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCOM®PC 740/4 GY1227-08LD is a polycarbonate (PC) product that contains fillers. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. ALCOM®The application fields of PC 740/4 GY1227-08LD include automobile industry and lighting equipment. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 23.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2450 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 66.0 | MPa | ISO 527-2 |
| -- | 66.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 6.0 | % | ISO 527-2 |
| Fracture | 70 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 3.5% strain | 76.0 | MPa | ISO 178 |
| -- | 100 | MPa | ISO 178 |
| Flexural Deflection at Max Force | 7.0 | % | ISO 178 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fire Behavior, FMVSS (1.00 mm) | passed | ISO 37 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Half Power Angle 1(1.00 mm) | 33.0 | ° |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 10 | kJ/m² | ISO 179/1eA |
| -40°C | 10 | kJ/m² | ISO 179/1eA |
| -20°C | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | No Break | ISO 179/1eU | |
| -40°C | No Break | ISO 179/1eU | |
| -20°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 124 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 142 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | HB | UL 94 | |
| 0.75 mm | V-2 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.0 mm | 850 | °C | IEC 60695-2-12 |
| 2.0 mm | 850 | °C | IEC 60695-2-12 |
| 3.0 mm | 850 960 | °C | IEC 60695-2-12 |
| 4.0 mm | 850 960 | °C | IEC 60695-2-12 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance 2(Total, 1000 µm) | 48.0 | % | ASTM D1003 |
| Haze 3(1000 µm) | 95 | % | ISO 13468 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Dehumidification desiccant | 100 - 120 | °C | |
| Hot air dryer | 100 - 120 | °C | |
| Drying Time | |||
| Dehumidification desiccant | 4.0 - 12 | hr | |
| Hot air dryer | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 270 - 310 | °C | |
| Mold Temperature | 80 - 110 | °C |
| Note Message | |
|---|---|
| 1 . | T(Y), A, 2° |
| 2 . | T(Y), A, 2° |
| 3 . | Ill. A, 2° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPTON™ 2104 | Kuraray Co., Ltd. | SEPS | SEPTON™ |
| Soarnol® E3808 | Soarus L.L.C. | EVOH | Soarnol® |
| VITAMIDE® AW33 | A. Schulman Europe | Nylon 66 | VITAMIDE® |
| ENVIROLON® ENV1266G33-NAT | ENVIROPLAS®, Inc. | Nylon 66 | ENVIROLON® |
| Plasmer 1050DB/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |