Badamid® LC70 M40
| Category: | Nylon 6+Nylon 66/6 , Polyamide 6 + PA 66/6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8bBhzq_Badamid-LC70-M40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Badamid® LC70 M40 is a Polyamide 6 + PA 66/6 (Nylon 6+Nylon 66/6) material filled with 40% mineral. It is available in Europe. Primary attribute of Badamid® LC70 M40: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.48 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.4 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6000 | 4000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 90.0 | 60.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 5.0 | 15 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 6.0 | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | -- | kJ/m² | |
| 23°C | 95 | 170 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 1 | 243 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 90 | 60 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 4.00 | 4.70 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.016 | 0.16 | IEC 60250 | |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propilven J-705 | Propilven, S.A. | PP Homopolymer | Propilven |
| MOSTEN GH 005 | UNIPETROL RPA | PP Homopolymer | MOSTEN |
| Epic Epoxy S7065-02 | Epic Resins | Epoxy | Epic Epoxy |
| Kumho SBR 1712P | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |
| Karina BLACK PVC COMPOUND 650-48/1-GARAP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |