LNP™ STAT-KON™ DEL329XF compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8ZulRc_LNPSTATKONDEL329XFcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* DEL329XF is a compound based on Polycarbonate resin containing Carbon Fiber, Flame Retardant, PTFE. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound DCL-4032 FR Product reorder name: DEL329XF |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.35 | g/cm³ | ASTM D792 |
| -- | 1.36 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/6.7 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 - 0.20 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.40 - 0.50 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.45 - 0.52 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.14 - 0.19 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.090 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.14 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7170 | MPa | ASTM D638 |
| -- | 7300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 92.0 | MPa | ASTM D638 |
| Fracture | 94.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.0 | % | ASTM D638 |
| Fracture | 1.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6480 | MPa | ASTM D790 |
| -- | 7300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 138 | MPa | ASTM D790 |
| -- | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 69 | J/m | ASTM D256 |
| 23°C 2 | 7.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 320 | J/m | ASTM D4812 |
| 23°C 3 | 22 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 15.2 | J | ASTM D3763 |
| -- | 2.72 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 143 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 141 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 139 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 138 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 2.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 4.2E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP512-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| SLOVAMID® 6 FRM 1 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| LAPEROS® T130 | Polyplastics Co., Ltd. | LCP | LAPEROS® |
| LNP™ STAT-KON™ ZE004 compound | SABIC Innovative Plastics | PPE+PS | LNP™ STAT-KON™ |
| Hostacom TRC 333N D82659 | LyondellBasell Industries | PP Copolymer | Hostacom |