DOWLEX™ 2645G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8YSR0b_DOWLEX-2645G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ Polyethylene Resin is designed for the production of a wide variety of film applications. Films made from this resin exhibit a combination of good toughness and tear resistance. Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.919 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Resistance (51 µm) | 16.6 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 168 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 238 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 14.2 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 14.6 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 48.8 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 39.2 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 620 | % | ASTM D882 |
| TD : Fracture, 51 µm | 740 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 300 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 720 | g | ASTM D1922 |
| TD : 51 µm | 1000 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 107 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 120 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 63 | ASTM D2457 | |
| Haze (50.8 µm) | 12 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm) 30:1 L/D 螺杆类型：DSBII 模具间隙：70 密尔 (1.8 mm) 输出：模具周长的 10 磅/小时/英寸 模具直径：6 英寸 放大比：2.5 : 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex WX-9120 | SAMSUNG SDI CO., LTD. | ASA | Starex |
| ADDILENE H 462 M20 | ADDIPLAST | PP Homopolymer | ADDILENE |
| Clariant Nylon 6/6 PA-113G13 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| ISORENE™ A4-1001 | SABIC Innovative Plastics Europe | TPE | ISORENE™ |
| LNP™ THERMOCOMP™ PF00DS compound | SABIC Innovative Plastics Europe | Nylon 6 | LNP™ THERMOCOMP™ |