ADVANCENE™ bEE-4906-AAH
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | ETHYDCO |
| Trademark: | ADVANCENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8XnDrw_ADVANCENEbEE4906AAH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADVANCENE™ bEE-4906-AAH is a thermally stabilized bimodal high molecular weight high density polethylene - hexene copolymer, produced using advanced gas phase PE process in a single reactor. It is intended for use in PE-100 pipe applications where the highest standards of long term hydrostatic strength and resistance to slow crack growth are esired. These high performance pipes can be used at higher pipeline operating pressures and have a potential to down-gauge. ADVANCENE™ bEE-4906-AAH has good processability with a high specific output (kg/hr/rpm), exceptional melt strength with very Low Sag, and good fusion compatibility. It is very suitable for large diameter and thick wall pipe but also for small diameter pipes. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.949 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 190°C/21.6 kg | 6.0 | g/10 min | ASTM D1238, ISO 1133 |
| 190°C/5.0 kg | 0.20 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 24.0 | MPa | ASTM D638, ISO 527-2 |
| Fracture | 26.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 500 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus - 2% Secant | 1000 | MPa | ASTM D790B, ISO 178 |
| Slow Crack Growth Resistance 1 | > 1000 | hr | ISO 13479 |
| Resistance to rapid crack propagation, Pc 2 | > 10.0 | bar | |
| Creep fracture strength 3 | > 200 | hr |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Designation | PE-100 | ISO 12162 | |
| Minimum Required Strength | > 10.0 | MPa | ISO 9080 |
| PENT - (slow crack growth; 80°C, 3.0 MPa) | > 1000 | hr | ASTM F1473 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.030 | % | |
| Cylinder Zone 1 Temp. | 190 - 210 | °C | |
| Cylinder Zone 3 Temp. | 190 - 210 | °C | |
| Cylinder Zone 5 Temp. | 190 - 210 | °C | |
| Melt Temperature | 200 - 220 | °C | |
| Die Temperature | 200 - 215 | °C |
| Note Message | |
|---|---|
| 1 . | Tested on 110mm SDR11 pipe |
| 2 . | Tested on 110mm SDR11 pipe |
| 3 . | Pressure test at 20°C and 12.4 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 2687B | Teknor Apex Company | TPV | Sarlink® TPV |
| Bio-Flex® F 1130 | FKuR Kunststoff GmbH | PLA | Bio-Flex® |
| HANWHA LLDPE 4300N | Hanwha Chemical | LLDPE | HANWHA LLDPE |
| Hifax TYC 1123X | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| FUDOWLITE® F5650F | Fudow Co., Ltd. | Phenolic | FUDOWLITE® |