OXPEKK® IG100
| Category: | PEKK , Polyetherketoneketone |
| Manufacturer: | Oxford Performance Materials, Inc. |
| Trademark: | OXPEKK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8WkUc5_OXPEKK-IG100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OXPEKK® IG100 is a Polyetherketoneketone (PEKK) material. It is available in Europe or North America. Typical application of OXPEKK® IG100: Medical/Healthcare |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (380°C/8.4 kg) | 35 to 40 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | < 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | < 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 86 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3450 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 103 | MPa | |
| Break | 89.6 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.0 | % | |
| Break | 80 | % | |
| Flexural Modulus | 3380 | MPa | ASTM D790 |
| Flexural Strength (5.0% Strain) | 138 | MPa | ASTM D790 |
| Compressive Strength | 103 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 141 | °C | ASTM D648 |
| Glass Transition Temperature | 155 | °C | DSC |
| Melting Temperature | 307 | °C | DSC |
| CLTE - Flow | 7.7E-5 | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ 09-325 Solution | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Moplen F39S | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Tufel® II 94505 | Momentive Performance Materials Inc. | Silicone | Tufel® II |
| AKROMID® B3 GF 50 9 RM-M natural (3698) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| FERREX® GPP20YJ13NA | Ferro Corporation | PP Homopolymer | FERREX® |