Microthene® G MN71020
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Microthene® G |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8WZm3o_Microthene-G-MN71020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Microthene G polyolefin powders are ground, irregularly-shaped particles designed for use in a broad range of specialty applications. Microthene G powders combine the unique properties of a polyolefin resin with a small, ground, particle size. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.915 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 22 | g/10 min | ASTM D1238 |
| Average Particle Size | 50 | mesh | |
| Particle Shape | Irregular |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore D | 49 | ||
| Shore D, 15 sec | 43 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 9.30 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 610 | % | ASTM D638 |
| Flexural Modulus | 228 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -34.6 | °C | ASTM D746 |
| Vicat Softening Temperature | 81.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 103 | °C | ASTM D3418 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9469-40D Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |
| Andur 8 APLF | Anderson Development Company | PUR-Ester/TDI | Andur |
| Ateva® 1821A | Celanese EVA Performance Polymers | EVA | Ateva® |
| Hanwha Total PE E210F | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | EVA | Hanwha Total PE |
| INEOS PP H13M-00 | INEOS Olefins & Polymers USA | PP Homopolymer | INEOS PP |