DOWLEX™ 2056G
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8WCwHS_DOWLEX-2056G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Puncture Energy | 1.58 | J | Internal method |
| Film Puncture Force | 62.3 | N | Internal method |
| Film Puncture Resistance | 25.2 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD | 115 | J/cm³ | ASTM D882 |
| TD | 128 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 174 | MPa | ASTM D882 |
| 2% secant, MD | 160 | MPa | ASTM D882 |
| 1% secant, TD | 179 | MPa | ASTM D882 |
| 2% secant, TD | 165 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 11.7 | MPa | ASTM D882 |
| TD : Yield | 12.0 | MPa | ASTM D882 |
| MD : Fracture | 49.6 | MPa | ASTM D882 |
| TD : Fracture | 41.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 700 | % | ASTM D882 |
| TD : Fracture | 550 | % | ASTM D882 |
| Dart Drop Impact | 220 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 400 | g | ASTM D1922 |
| TD | 600 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 102 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 119 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°) | 26 | ASTM D2457 | |
| Haze | 23 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：3.5 英寸 螺杆类型：DSB II 模具间隙：70 密尔 (1.8 mm) 熔体温度：419°F 输出：模具周长的 12 磅/小时/英寸 模具直径：8 英寸 放大比：2.5:1 螺杆速度：39 rpm 冷冻线高度：39 英寸 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 86012-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| AFFINITY™ GA 1000R | The Dow Chemical Company | TPO (POE) | AFFINITY™ |
| HiFill® PA6 GF/M25 HS L BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Karina WHITE PVC COMPOUND 801-10/ 49-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® ABS 7000 | Techmer Engineered Solutions | ABS | Plaslube® |