Order Products : sales@su-jiao.com
Larton MDT16-02
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Larton |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 8Vz3IG_Larton-MDT16-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyphenylene Sulphide (PPS) based compound. Magnetic detectable filler. Very good chemical resistance. Very good thermal properties. Low smoke density and low toxicity index. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.77 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.35 to 0.50 | % | |
| Flow : 2.00 mm | 0.35 to 0.50 | % | |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 14500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 60.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 0.50 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 180 | °C | ISO 75-2/A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 290 to 310 | °C | |
| Mold Temperature | 130 to 140 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Boltaron 4005 | Boltaron Performance Products | PVC, Unspecified | Boltaron |
| COPYLENE® CR020CL | Phillips 66 | PP Random Copolymer | COPYLENE® |
| Elastron® G P.G100.A70.B | Elastron USA, Inc. | SEBS | Elastron® G |
| OXPEKK® IG200 | Oxford Performance Materials, Inc. | PEKK | OXPEKK® |
| Plenco 01510 (Transfer) | Plastics Engineering Co. | Polyester, TS | Plenco |